Optimization of Eco-Friendly Cement Composition Based on Fly Ash in Geopolymer Concrete Mortar Production

Arwanto Arwanto; Firdaus Firdaus

doi:10.55927/fjst.v4i9.237

Authors

Arwanto Arwanto Universitas Bina Darma Palembang
Firdaus Firdaus Universitas Bina Darma Palembang

DOI:

https://doi.org/10.55927/fjst.v4i9.237

Keywords:

Eco-Friendly Cement, Geopolymer, Fly Ash Based, Dry Mix Method

Abstract

This study develops geopolymer cement using a dry mix method, replacing Portland cement with fly ash and utilizing solid Na₂SiO₃ derived from rice husk ash. Paste and mortar samples with three mix variations were tested for setting time and compressive strength. The initial setting time ranged from 75 minutes, while the final setting time reached up to 360 minutes. The highest compressive strength was 26 MPa for paste at 14 days and 20 MPa for mortar at 56 days. The results confirm the feasibility of producing environmentally friendly geopolymer cement with this method, though further research is needed to improve compressive strength and apply it in concrete production.

References

Erniati Bachtiar. 2019, Material Ramah Lingkungan “Mortar Geopolymer-Fly Ash”, Fakultas Teknik Universitas Fajar.

Marthin, D. J. Sumajouw, Servie O Dapas 2013, Elemen Struktur Beton Bertulang Geopolymer, Andi Yogyakarta.

NI 1974:2011, ICS 91.100.30, 2011. Cara Uji Kuat Tekan Beton dengan Benda Uji Silinder, Badan Standardisasi Nasional, Jakarta.

“Firdaus, handoko barata yuda, 2019, Waktu Ikat Mortar “ Semen “ Geopolymer Berbasis Fly Ash Dan Kapur, Program Studi Teknik Sipil Universitas Bina Darma Palembang.

Abdul Karim Yasin, 2017, Rekayasa Beton Geopolimer Berbasis Fly Ash, Institut Teknologi Sepuluh Nopember Surabaya.

ASTM C191-21, Standard Test Methods for Time of Setting of Hydraulic Cement by Vicat Needle1.

ASTM C496M – 11, Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens1.

Edowinsyah, Firdaus, 2021, Lightweight Mortar, Geopolimer Based On Fly Ash And Palm Ash, Magister Teknik Sipil , Universitas Bina Darma, Palembang, Idnonesia

ko Sulistiyono, Sumantri Sastra wiguna dan Djusman Sajuti, 2004, Kajian proses pembentukan jel dan pengendapan silika, Pusat Penelitian Metalurgi (P2M) – LIPI.

F ki Riki Tambingon, Marthin D. J. Sumajouw, Steenie E. Wallah, 2017, Kuat Tekan Beton Geopolymer Dengan Perawatan Temperatur Ruangan, FT. Universitas Sam Ratulangi Manado.

Ir. Nurly Gofar, Ph.D., Dr. Ir. Achmad Syarifudin, M.Eng., Dr. Firdaus, ST. MT., Yuzan Kalpataru, M.Kom., Dian Rianawati, SE., MM., Dendi Triadi, M.Kom., 2019, Pedoman Penyusunan Tesis, Program Pascasarjana Universitas Bina Darma.

Linda Trivana, Sri Sugiarti dan Eti Rohaeti, 2015, Sintesis Dan Karakterisasi Natrium Silikat (Na2SiO3) Dari Sekam Padi, Balai Penelitian Tanaman Palma Manado, Institut Pertanian Bogor, Fakultas MIPA, Jurusan Kimia.

Rulli Ranastra Irawan, Setyo Hardono, Yanu Ikhtiar Budiman, Ogi Soeherman, Desak Nyoman Deasy Triani & Gugun Gunawan 2015, beton dengan sedikit semen portland dan tanpa semen Portland memanfaatkan abu terbang dari pltu batubara, pusat penelitian dan pengembangan jalan dan jembatan.

S. Nagajothi, S. Elavenil, S. Angalaeswari, L. Natrayan, and Wubishet Degife Mammo, 2022, Durability Studies on Fly Ash Based Geopolymer Concrete Incorporated with Slag and Alkali Solutions, School of Civil Engineering, Vellore Institute Technology, Chennai, Tamil Nadu, India.

Sirin Fairus, Haryono, Mas H. Sugita, dan Agus Sudrajat, 2009, proses pembuatan water glass dari pasir silika dengan pelebur natrium hidroksida, Institut Teknonogi Nasional, Fakultas Teknologi Industri, Jurusan Teknik Kimia